Cobalt Alloy Haynes 188 Sheet in Mumbai, Cobalt Alloy Haynes 188 Sheet Importers in Mumbai, Cobalt Alloy Haynes 188 Sheet Suppliers in Mumbai, Cobalt Alloy Haynes 188 Sheet Exporters in Mumbai, Cobalt Alloy Haynes 188 Sheet Stockists in Mumbai.
Haynes 188™ is a cobalt based alloy with excellent high temperature strength and great oxidation resistance up to 2000° F. Haynes 188’s™ has good resistance to sulfidation and good metallurgical stability, therefore Haynes 188™ can be easily fabricated.
Element
Min
Max
Carbon
0.05
0.15
Manganese
--
1.25
Silicon
0.20
0.50
Phosphorus
--
0.02
Sulfur
--
0.015
Chromium
21.0
23.0
Nickel
20.0
24.0
Tungsten
13.0
15.0
Lanthanum
0.03
0.12
Boron
--
0.015
Iron
--
3.0
Cobalt
Bal.
Physical Properties
Physical Properties
°F
British Units
°C
Metric Units
Density
72
0.324 lb./in.(3)
22
8.98 g/cm(3)
Incipient Fusion
Temperature
2375-
2425
1302-
1330--
Electrical
Resistivity
70
39.6 microhm-in.
21
1.01 microhm-m
Mean Coefficient
of Thermal
Expansion
70 to -400
5.4 microin./in.-°F
21 to -200
9.7 X 10(-6)m/m-K
70 to -200
5.8 microin./in.-°F
21 to -129
10.4 X 10(-6)m/m-K
70-0
6.2 microin./in.-°F
21 to -18
11.2 X 10(-6)m/m-K
70-100
6.2 microin./in.-°F
21-38
11.5 X 10(-6)m/m-K
70-200
6.6 microin./in.-°F
21-93
11.9 X 10(-6)m/m-K
70-400
7.0 microin./in.-°F
21-204
12.6 X 10(-6)m/m-K
70-600
7.4 microin./in.-°F
21-316
13.3 X 10(-6)m/m-K
70-800
7.8 microin./in.-°F
21-427
14.0 X 10(-6)m/m-K
70-1000
8.2 microin./in.-°F
21-538
14.8 X 10(-6)m/m-K
70-1200
8.6 microin./in.-°F
21-649
15.5 X 10(-6)m/m-K
70-1400
9.0 microin./in.-°F
21-760
16.2 X 10(-6)m/m-K
70-1600
9.4 microin./in.-°F
21-871
16.9 X 10(-6)m/m-K
70-1800
9.9 microin./in.-°F
21-982
17.8 X 10(-6)m/m-K
70-2000
10.3 microin./in.-°F
21-1093
18.5 X 10(-6)m/m-K
Thermal
Conductivity
100
75 Btu-in/ft²-hr-°F
38
10.8 W/m-K
400
100 Btu-in/ft²-hr-°F
204
14.4 W/m-K
600
112 Btu-in/ft²-hr-°F
316
16.1 W/m-K
800
125 Btu-in/ft²-hr-°F
427
18.0 W/m-K
1000
138 Btu-in/ft²-hr-°F
538
19.9 W/m-K
1200
152 Btu-in/ft²-hr-°F
649
21.9 W/m-K
1400
167 Btu-in/ft²-hr-°F
760
24.1 W/m-K
Thermal
Diffusivity
572
0.006 in²/sec
300
3.9 x 10(-6)m²/s
752
0.006 in²/sec
400
3.9 x 10(-6)m²/s
932
0.007 in²/sec
500
4.5 x 10(-6)m²/s
1112
0.007 in²/sec
600
4.5 x 10(-6)m²/s
1409
0.008 in²/sec
765
5.2 x 10(-6)m²/s
1652
0.008 in²/sec
900
5.2 x 10(-6)m²/s
2012
0.009 in²/sec
1100
5.8 x 10(-6)m²/s
Magnetic Permeability
(Room Temperature)
1.01 at 200 oersteds (15,900 A/m)
2 notes
·
View notes
Text
Cobalt Alloy Haynes 188 Sheet Suppliers in Mumbai
Cobalt Alloy Haynes 188 Sheet, Cobalt Alloy Haynes 188 Sheet Importers, Cobalt Alloy Haynes 188 Sheet Suppliers, Cobalt Alloy Haynes 188 Sheet Exporter, Cobalt Alloy Haynes 188 Sheet Stockists.
Cobalt Alloy Haynes 188 Sheet in India, Cobalt Alloy Haynes 188 Sheet Importers in India, Cobalt Alloy Haynes 188 Sheet Suppliers in India, Cobalt Alloy Haynes 188 Sheet Exporter in India, Cobalt Alloy Haynes 188 Sheet Stockists in India.
Cobalt Alloy Haynes 188 Sheet in Mumbai, Cobalt Alloy Haynes 188 Sheet Importers in Mumbai, Cobalt Alloy Haynes 188 Sheet Suppliers in Mumbai, Cobalt Alloy Haynes 188 Sheet Exporters in Mumbai, Cobalt Alloy Haynes 188 Sheet Stockists in Mumbai.
Haynes 188™ is a cobalt based alloy with excellent high temperature strength and great oxidation resistance up to 2000° F. Haynes 188’s™ has good resistance to sulfidation and good metallurgical stability, therefore Haynes 188™ can be easily fabricated.
Element
Min
Max
Carbon
0.05
0.15
Manganese
--
1.25
Silicon
0.20
0.50
Phosphorus
--
0.02
Sulfur
--
0.015
Chromium
21.0
23.0
Nickel
20.0
24.0
Tungsten
13.0
15.0
Lanthanum
0.03
0.12
Boron
--
0.015
Iron
--
3.0
Cobalt
Bal.
Physical Properties
Physical Properties
°F
British Units
°C
Metric Units
Density
72
0.324 lb./in.(3)
22
8.98 g/cm(3)
Incipient Fusion
Temperature
2375-
2425
1302-
1330--
Electrical
Resistivity
70
39.6 microhm-in.
21
1.01 microhm-m
Mean Coefficient
of Thermal
Expansion
70 to -400
5.4 microin./in.-°F
21 to -200
9.7 X 10(-6)m/m-K
70 to -200
5.8 microin./in.-°F
21 to -129
10.4 X 10(-6)m/m-K
70-0
6.2 microin./in.-°F
21 to -18
11.2 X 10(-6)m/m-K
70-100
6.2 microin./in.-°F
21-38
11.5 X 10(-6)m/m-K
70-200
6.6 microin./in.-°F
21-93
11.9 X 10(-6)m/m-K
70-400
7.0 microin./in.-°F
21-204
12.6 X 10(-6)m/m-K
70-600
7.4 microin./in.-°F
21-316
13.3 X 10(-6)m/m-K
70-800
7.8 microin./in.-°F
21-427
14.0 X 10(-6)m/m-K
70-1000
8.2 microin./in.-°F
21-538
14.8 X 10(-6)m/m-K
70-1200
8.6 microin./in.-°F
21-649
15.5 X 10(-6)m/m-K
70-1400
9.0 microin./in.-°F
21-760
16.2 X 10(-6)m/m-K
70-1600
9.4 microin./in.-°F
21-871
16.9 X 10(-6)m/m-K
70-1800
9.9 microin./in.-°F
21-982
17.8 X 10(-6)m/m-K
70-2000
10.3 microin./in.-°F
21-1093
18.5 X 10(-6)m/m-K
Thermal
Conductivity
100
75 Btu-in/ft²-hr-°F
38
10.8 W/m-K
400
100 Btu-in/ft²-hr-°F
204
14.4 W/m-K
600
112 Btu-in/ft²-hr-°F
316
16.1 W/m-K
800
125 Btu-in/ft²-hr-°F
427
18.0 W/m-K
1000
138 Btu-in/ft²-hr-°F
538
19.9 W/m-K
1200
152 Btu-in/ft²-hr-°F
649
21.9 W/m-K
1400
167 Btu-in/ft²-hr-°F
760
24.1 W/m-K
Thermal
Diffusivity
572
0.006 in²/sec
300
3.9 x 10(-6)m²/s
752
0.006 in²/sec
400
3.9 x 10(-6)m²/s
932
0.007 in²/sec
500
4.5 x 10(-6)m²/s
1112
0.007 in²/sec
600
4.5 x 10(-6)m²/s
1409
0.008 in²/sec
765
5.2 x 10(-6)m²/s
1652
0.008 in²/sec
900
5.2 x 10(-6)m²/s
2012
0.009 in²/sec
1100
5.8 x 10(-6)m²/s
Magnetic Permeability
(Room T
0 notes
Text
Cobalt Alloy Haynes 188 Sheet Importers
Haynes 188™ is a cobalt based alloy with excellent high temperature strength and great oxidation resistance up to 2000° F. Haynes 188’s™ has good resistance to sulfidation and good metallurgical stability, therefore Haynes 188™ can be easily fabricated.
Element Min Max
Carbon 0.05 0.15
Manganese -- 1.25
Silicon 0.20 0.50
Phosphorus -- 0.02
Sulfur -- 0.015
Chromium 21.0 23.0
Nickel 20.0 24.0
Tungsten 13.0 15.0
Lanthanum 0.03 0.12
Boron -- 0.015
Iron -- 3.0
Cobalt Bal.
For more information :
Visit our website: https://www.aluminiumwala.com/cobalt-alloy-haynes-188-sheet-suppliers-stockists-importers-exporters.html
Contact Us : +91 916 734 7029
Email : [email protected]
#Cobalt Alloy Haynes 188 Sheet#Cobalt Alloy Haynes 188 Sheet Importers#Cobalt Alloy Haynes 188 Sheet Suppliers#Cobalt Alloy Haynes 188 Sheet Exporter#Cobalt Alloy Haynes 188 Sheet Stockists.#Cobalt Alloy Haynes 188 Sheet in India#Cobalt Alloy Haynes 188 Sheet Importers in India#Cobalt Alloy Haynes 188 Sheet Suppliers in India#Cobalt Alloy Haynes 188 Sheet Exporter in India#Cobalt Alloy Haynes 188 Sheet Stockists in India.
1 note
·
View note
Text
Cobalt Nickel 188 Sheet
Alloy 188 is a cobalt-nickel-chromium-tungsten super alloy that is sold under different brand names including: Nickel Alloy 188, Haynes® 188, Udimet 188®. Due to its high level of chromium mixed with small amounts of lanthanum, Alloy 188 can be used to create products that are incredibly tough and corrosion resistant.
Alloy 188 provides an excellent high-temperature strength, suflidation resistance, and good oxidation resistance up to 2000 °F (1095°C). Fabrication is not difficult with Alloy 188, and it can be cold and hot worked, and offers users outstanding ductility and metallurgical stability.
For More Information:
Visit Our Website: https://www.aluminiumwala.com/
Contact No: +91 916 734 7029
E-Mail ID: [email protected]
6 notes
·
View notes
Text
Alloy 188 Sheet Suppliers in India
Super alloy Alloy 188, also known as Nickel Alloy 188, Haynes® 188, and Udimet 188®, is a cobalt, nickel, chromium, and tungsten combination. Alloy 188's high chromium content combined with trace levels of lanthanum makes it ideal for use in manufacturing extremely durable and corrosion-resistant items.
To 2000 °F (1095 °C), alloy 188 has exceptional oxidation resistance, outstanding high-temperature strength, and suflidation resistance. Alloy 188 has exceptional ductility and metallurgical stability, and it is easy to fabricate using both cold and hot processes.
Additionally, alloy 188 works well with TIG, MIG, electron beam, and resistance welding techniques.
Alloy 188 is used in a wide range of gas turbine engine and aerospace applications.
For More Information:
Visit Our Website: https://www.aluminiumwala.com/
Contact No: +91 916 734 7029
E-Mail ID: [email protected]
2 notes
·
View notes
Text
Haynes 188 Sheet Suppliers in India
Haynes 188 Sheet in Mumbai, Haynes 188 Sheet Importers in Mumbai, Haynes 188 Sheet Suppliers in Mumbai, Haynes 188 Sheet Exporters in Mumbai, Haynes 188 Sheet Stockists in Mumbai.
HAYNES 188 Sheets is a cobalt-nickel-chromium-tungsten alloy that may be readily fabricated for aerospace and commercial gas turbine engine applications, including combustion cans, flame holders, liners, transition ducts, and afterburner parts. HAYNES 188 Coils is generally found in hot sections of engines in burner cans, ducting and afterburner components. In recent years, Udimet 188 Coils has been eclipsed by Alloy 230 for many applications due to improved properties. Udimet 188 Plates has good forming characteristics and is capable of being forged, hot worked or cold worked, although it does work-harden very rapidly so frequent intermediate annealing treatments are recommend for complex forming operations. Buy Alloy 188 Plates at reasonable price from us.
What are Haynes 188 Plates?
Haynes 188 Plate is a cobalt-based alloy that is composed of nickel, chromium, tungsten, and molybdenum, along with other elements. It is known for its excellent high-temperature strength, resistance to corrosion and oxidation, and good weldability.
What are the properties of Haynes 188 plates?
Haynes 188 plates have excellent high-temperature strength, good oxidation resistance, and good resistance to corrosion and erosion. They also have good weldability and formability, making them suitable for a wide range of industrial applications.
What are the applications of Haynes 188 plates?
Haynes 188 plates are commonly used in high-temperature applications, such as gas turbine components, exhaust systems, and heat exchangers. They are also used in chemical processing, power generation, and aerospace applications.Specifications:AMS 5608 / AMS 5609Standard:AMS, AMS and APISpecialize:Shim Sheet, Perforated Sheet, B. Q. Profile.Size:0.5 MM TO 200 MM THICK IN 1000 MM TO 2500 MM WIDTH & 2500 MM TO 12500 MM LENGTHForm:Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange)Finish:Hot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated)Hardness:Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc.Grade:Haynes 188 (UNS R30188)
Haynes 188 Plates Equivalent Grades
STANDARDWERKSTOFF NR.UNSHaynes 188–R30188
188 Haynes Plates Chemical Composition :
GradeCMnpSSiCrNiCoBFeLaWHaynes 18805-151.25
max020
max.015 max20-.5021.0
-23.020.0
-24.0Bal.015
max3.0
max03-1513.0
-15.0
Special Products
Haynes 188 Sheet
Alloy 188 Sheet
Conicro 4023 Sheet
2.4683 Sheet
Uns R30188 Sheet
Cobalt Alloy Haynes 188 Sheet
AMS 5772 Sheet
Cobalt Nickel 188 Sheet
Stellite 188 Sheet
Haynes 25 Sheet
L605 Sheet
Udimet L605 Sheet
Stellite 25 Sheet
UNS R30605 Sheet
2.4964 Sheet
AMS 5537 Sheet
Ams 5759 Sheet
HS25 Sheet
Cocr20w15ni Sheet
Cobalt Alloy Haynes 25 Sheet
Cobalt L605 Sheet
Inconel X750 Sheet
X750 Sheet
Haynes X750 Sheet
Nicrofer 7016 Sheet
Udimet X750 Sheet
Pyromet X750 Sheet
Superimphy 750 Sheet
2.4669 Sheet
UNS N07750 Sheet
Nickel Alloy X750 Sheet
NiCr15Fe7TiAl Sheet
Nickelvac X750 Sheet
AMS 5699 Sheet
Alloy X750 Sheet
Nimonic C263 Sheet
Nickel Alloy C263 Sheet
UNS N07263 Sheet
Haynes 263 Sheet
2.4650 Sheet
NiCo20Cr20MoTi Sheet
AMS 5872 Sheet
Hastelloy C263 Sheet
Nicrofer 5120 Coti Sheet
Nicrofer 5120 Coti Round Bar
Inconel 945 Round
Inconel 945 Bar
UNS N09945 Round
Inconel 945X Round
2 notes
·
View notes
Text
Haynes 188 Sheet Suppliers in India
HAYNES 188 Sheets is a cobalt-nickel-chromium-tungsten alloy that may be readily fabricated for aerospace and commercial gas turbine engine applications, including combustion cans, flame holders, liners, transition ducts, and afterburner parts. HAYNES 188 Coils is generally found in hot sections of engines in burner cans, ducting and afterburner components. In recent years, Udimet 188 Coils has been eclipsed by Alloy 230 for many applications due to improved properties. Udimet 188 Plates has good forming characteristics and is capable of being forged, hot worked or cold worked, although it does work-harden very rapidly so frequent intermediate annealing treatments are recommend for complex forming operations. Buy Alloy 188 Plates at reasonable price from us.
0 notes
Text
Uns R30188 Sheet
Haynes 188 alloy is often referred to by other trade names such as Alloy 188, Udimet 188, and Conicro 4023. Haynes 188 is a cobalt-nickel-chromium-tungsten alloy that may be readily fabricated for aerospace and commercial gas turbine engine applications, including combustion cans, flame holders, liners, transition ducts, and afterburner parts. Haynes 188 alloy also combines excellent high-temperature strength with very good resistance to oxidizing environments up to 2000°F (1095°C).
Other features include superior resistance to molten chloride salts and resistance to gaseous sulfidation.
For More Information:
Visit Our Website: https://www.aluminiumwala.com/
Contact No: +91 916 734 7029
E-Mail ID: [email protected]
0 notes
Text
Uns R30188 Sheet Suppliers
Haynes 188 alloy is often referred to by other trade names such as Alloy 188, Udimet 188, and Conicro 4023. Haynes 188 is a cobalt-nickel-chromium-tungsten alloy that may be readily fabricated for aerospace and commercial gas turbine engine applications, including combustion cans, flame holders, liners, transition ducts, and afterburner parts. Haynes 188 alloy also combines excellent high-temperature strength with very good resistance to oxidizing environments up to 2000°F (1095°C).
0 notes
Text
Uns R30188 Sheet
Haynes 188 alloy is often referred to by other trade names such as Alloy 188, Udimet 188, and Conicro 4023. Haynes 188 is a cobalt-nickel-chromium-tungsten alloy that may be readily fabricated for aerospace and commercial gas turbine engine applications, including combustion cans, flame holders, liners, transition ducts, and afterburner parts.
Haynes 188 alloy also combines excellent high-temperature strength with very good resistance to oxidizing environments up to 2000°F (1095°C).
Other features include superior resistance to molten chloride salts and resistance to gaseous sulfidation.
For More Information:
Visit Our Website: https://www.aluminiumwala.com/
Contact No: +91 916 734 7029
E-Mail ID: [email protected]
0 notes
Text
Uns R30188 Sheet Exporters in Mumbai
There are several commercial names for Haynes 188 alloy, including Conicro 4023, Udimet 188, and Alloy 188. Combustion cans, flame holders, liners, transition ducts, and afterburner pieces are among the parts that can be easily made from Haynes 188, an alloy consisting of cobalt, nickel, chromium, and tungsten, for industrial and aerospace gas turbine engines. exceptional resistance to oxidizing conditions up to 2000°F (1095°C) and exceptional high-temperature strength are also combined in the Haynes 188 alloy.
Better resistance to molten chloride salts and resistance to gaseous sulfidation are two further benefits.
For More Information:
Visit Our Website: https://www.aluminiumwala.com/
Contact No: +91 916 734 7029
E-Mail ID: [email protected]
0 notes
Text
Uns R30188 Sheet
Haynes 188 alloy is often referred to by other trade names such as Alloy 188, Udimet 188, and Conicro 4023. Haynes 188 is a cobalt-nickel-chromium-tungsten alloy that may be readily fabricated for aerospace and commercial gas turbine engine applications, including combustion cans, flame holders, liners, transition ducts, and afterburner parts. Haynes 188 alloy also combines excellent high-temperature strength with very good resistance to oxidizing environments up to 2000°F (1095°C).
For More Information:
Visit Our Website: https://www.aluminiumwala.com/
Contact No: +91 916 734 7029
E-Mail ID: [email protected]
0 notes
Text
Cobalt Alloy Haynes 188 Sheet Suppliers in India
Haynes 188™ is a cobalt based alloy with excellent high temperature strength and great oxidation resistance up to 2000° F. Haynes 188’s™ has good resistance to sulfidation and good metallurgical stability, therefore Haynes 188™ can be easily fabricated.
0 notes
Text
Haynes 188 Sheet, Haynes 188 Sheet Importers, Haynes 188 Sheet Suppliers, Haynes 188 Sheet Exporter, Haynes 188 Sheet Stockists.
Haynes 188 Sheet in India, Haynes 188 Sheet Importers in India, Haynes 188 Sheet Suppliers in India, Haynes 188 Sheet Exporter in India, Haynes 188 Sheet Stockists in India.
Haynes 188 Sheet in Mumbai, Haynes 188 Sheet Importers in Mumbai, Haynes 188 Sheet Suppliers in Mumbai, Haynes 188 Sheet Exporters in Mumbai, Haynes 188 Sheet Stockists in Mumbai.
HAYNES 188 Sheets is a cobalt-nickel-chromium-tungsten alloy that may be readily fabricated for aerospace and commercial gas turbine engine applications, including combustion cans, flame holders, liners, transition ducts, and afterburner parts. HAYNES 188 Coils is generally found in hot sections of engines in burner cans, ducting and afterburner components. In recent years, Udimet 188 Coils has been eclipsed by Alloy 230 for many applications due to improved properties. Udimet 188 Plates has good forming characteristics and is capable of being forged, hot worked or cold worked, although it does work-harden very rapidly so frequent intermediate annealing treatments are recommend for complex forming operations. Buy Alloy 188 Plates at reasonable price from us.
What are Haynes 188 Plates?
Haynes 188 Plate is a cobalt-based alloy that is composed of nickel, chromium, tungsten, and molybdenum, along with other elements. It is known for its excellent high-temperature strength, resistance to corrosion and oxidation, and good weldability.
What are the properties of Haynes 188 plates?
Haynes 188 plates have excellent high-temperature strength, good oxidation resistance, and good resistance to corrosion and erosion. They also have good weldability and formability, making them suitable for a wide range of industrial applications.
What are the applications of Haynes 188 plates?
Haynes 188 plates are commonly used in high-temperature applications, such as gas turbine components, exhaust systems, and heat exchangers. They are also used in chemical processing, power generation, and aerospace applications.Specifications:AMS 5608 / AMS 5609Standard:AMS, AMS and APISpecialize:Shim Sheet, Perforated Sheet, B. Q. Profile.Size:0.5 MM TO 200 MM THICK IN 1000 MM TO 2500 MM WIDTH & 2500 MM TO 12500 MM LENGTHForm:Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange)Finish:Hot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated)Hardness:Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc.Grade:Haynes 188 (UNS R30188)
Haynes 188 Plates Equivalent Grades
STANDARDWERKSTOFF NR.UNSHaynes 188–R30188
188 Haynes Plates Chemical Composition :
GradeCMnpSSiCrNiCoBFeLaWHaynes 18805-151.25
max020
max.015 max20-.5021.0
-23.020.0
-24.0Bal.015
max3.0
max03-1513.0
-15.0
0 notes
Text
Haynes 25 Sheet Stockists in India
HAYNES® 25 alloy (UNS R30605) is a cobalt-nickel- chromium-tungsten alloy that combines excellent high-temperature strength with good resistance to oxidizing environments up to 1800°F (980°C) for prolonged exposures, and excellent resistance to sulfidation. It can be fabricated and formed by conventional techniques, and has been used for cast components. Other attractive features include excellent resistance to metal galling.
Haynes 25™ alloy is the strongest of all the fabricable cobalt alloys. It has an excellent temperature strength and oxidation resistance to 2000 °F. However, Haynes 25™ cobalt alloy is hot formable between 1900 ≥F- 2300 °F. In addition, it is better to cold-work alloy L605 for bending, spinning and drawing component processes.
HAYNES® 25 alloy has good forming and welding characteristics. It may be forged or otherwise hot-worked, providing that it is held at 2200°F (1205°C) for a time sufficient to bring the entire piece to temperature. The alloy has good ductility, and thus also may be formed by cold working. The alloy does work-harden very rapidly, however, so frequent intermediate annealing treatments will be needed for complex component forming operations. All hot- or cold-worked parts should be annealed and rapidly cooled in order to restore the best balance of properties. The alloy can be welded by both manual and automatic welding methods, including gas tungsten arc (GTAW), gas metal arc (GMAW), shielded metal arc, electron beam and resistance welding. It exhibits good restraint welding characteristics.
Features :
Meets AMS 5537 specifications
Meets AMS 5796 specifications
Enormously beneficial high temperature strength
Provides oxidation resistance up to 1800° F
Galling resistant
Resistant to acids, body fluids and marine environments
Applications :
HAYNES® 25 alloy combines properties which make it suitable for a number of component applications in the aerospace industry, including parts in established military and commercial gas turbine engines. In modern engines, it has largely been replaced by newer materials such as HAYNES® 188 alloy, and, most recently, 230® alloy, which possess improved properties. Another area of significant usage for 25 alloy is as a bearing material, for both balls and races.
Specifications :
UNS: R30605
Specifications: AMS 5537
International Specifications: Werkstoff Nr. 2.4964
For more information :
Visit our website : https://www.aluminiumwala.com/haynes-25-sheet-suppliers-stockists-importers-exporters.html
Contact Us : +91 916 734 7029
Email Id : [email protected]
1 note
·
View note
Text
Alloy 188 Sheet Importers
Alloy 188 is a cobalt-nickel-chromium-tungsten super alloy that is sold under different brand names including: Nickel Alloy 188, Haynes® 188, Udimet 188®. Due to its high level of chromium mixed with small amounts of lanthanum, Alloy 188 can be used to create products that are incredibly tough and corrosion resistant.
Alloy 188 provides an excellent high-temperature strength, suflidation resistance, and good oxidation resistance up to 2000 °F (1095°C). Fabrication is not difficult with Alloy 188, and it can be cold and hot worked, and offers users outstanding ductility and metallurgical stability.
Alloy 188 is also well suited for welding, methods such TIG, MIG, electron beam, and resistance welding.
Alloy 188, in all its forms, is found in many different aerospace and gas turbine engine applications including:
Flame holders
Transition ducts
Afterburner liners
Combustion cans
Spray bars
The chemical composition of Alloy 188 is unique and includes:
Co 39% balance
Ni 20-24%
Cr 21-23%
W 13-15%
Mn 1.25% max
Fe 3% max
If you are looking for a nickel alloy for extreme-temperature applications that is also easy to work with and versatile, Alloy 188 is an excellent choice. Continental Steel can supply Nickel Alloy 188, Haynes® 188, Udimet® 188 in bar, strip, sheet, and wire.
For more information :
Visit our website: https://www.aluminiumwala.com/alloy-188-sheet-suppliers-stockists-importers-exporters.html
Contact Us : +91 916 734 7029
Email : [email protected]
#Plus Metals#Alloy 188 Sheet#Alloy 188 Sheet Importers#Alloy 188 Sheet Suppliers#Alloy 188 Sheet Exporter#Alloy 188 Sheet Stockists#Alloy 188 Sheet in India#Alloy 188 Sheet Importers in India#Alloy 188 Sheet Suppliers in India
0 notes
Last Seen Blogs
famira
FAMIRA ICONS
communist-sasuke
sasuke was right
amyfrachiseur
Untitled
9jatinzmedia
9jatinz
couplefavorst
Credit peoples fizzle